Acrylate Rubber, Acrylic Rubber, ACM has excellent heat resistant and oilproof performance. It could be used in temperatures from--30 upto +180 degrees Celsius. Acrylate Rubber, Acrylic Rubber, ACM is also called as vehicle rubber which is a suitable materials for rubber oil seals, o rings, gaskets, hoses for high temperature usage. Acrylate Rubber, Acrylic Rubber, ACM has others excellent performances like ozone resistance, good flexibility, light aging resistance, good airtightness, rubber transparency, good adhesiveness on fabrics, etc. So Acrylate Rubber, Acrylic Rubber, ACM has wide application fields in sponges, deep prospecting, electric apparatus to replace silicone, adhesive. Rimpex Rubber supplies 3 models of Acrylate Rubber, Acrylic Rubber, ACM as following:
ACM91, ACM95, ACM96 and ACM Compounds
Technical Parameters of Acrylate Rubber, Acrylic Rubber (ACM Compounds) for O Rings
Model |
ACM95 |
ACM96 |
ACM91 |
|
| Tensile Strength at Break, MPa | 10-15 |
10-16 |
10-17 |
|
| Hardness, Shore Durometers | 40-90 |
40-90 |
40-80 |
|
| Maximum Tensile Elongation, % | 200-300 |
200-300 |
200-350 |
|
| Permanent Deformation, %, Less Than | 20 |
20 |
20 |
|
| Brittleness Temperature, Degree Celsius, Less Than | -15 |
-25 |
-35 |
|
| Compression Permanent Deformation, 150℃*70h 25% | 25-45 |
25-45 |
25-45 |
|
| Hot Air Aging, 150℃*70h | Tension Strength Variation, % | ±20 |
±20 |
±20 |
| Breakage Elongation Variation, % | ±20 |
±20 |
±20 |
|
| Hardness Variation, % | 0-10 |
0-10 |
0-10 |
|
| #3 Standard Oil, 150℃*70h | Volume Change, % | 5-15 |
5-15 |
5-15 |
| Machining Performance | Excellent |
Excellent |
Excellent |
|
Technical Parameters of Acrylate Rubber, Acrylic Rubber (ACM Compounds) for Oil Seals
Model |
ACM95 |
ACM96 |
ACM91 |
|
| Hardness, Shore Durometers | 40-90 |
40-90 |
40-90 |
|
| Tensile Strength, Kgt/cm | >12 |
>11 |
>11 |
|
| Maximum Tensile Elongation, % | 180-350 |
200-350 |
200-350 |
|
| Tearing Strength, Kgt/cm | 20-35 |
20-35 |
15-35 |
|
| 25% Compression Permanent Deformation, 150℃*70h | 25-45 |
25-45 |
30-50 |
|
| Service Temperature, Degree Celsius | -20~+180 |
-28~+180 |
-40~+180 |
|
| Hot Air Aging, 175℃*70h | Breakage Elongation Variation, % | -30 |
-30 |
-30 |
| Breakage Tensile Strength Variation, % | -10 |
-10 |
-10 |
|
| #1 Anti-Medium Oil, Maximum Volume Change, % | -1~+3 |
-2~+3 |
-1~+3 |
|
| #3 Anti-Medium Oil, Maximum Volume Change, % | 0~+15 |
0~+15 |
0~+15 |
|
| Machining Performance | Excellent |
Excellent |
Excellent |
|
ACM Compounds for Extrusion Hoses
ACM Compounds for Vehicle Oilproof Rubber Hoses
Technical Parameters of Acrylate Rubber, Acrylic Rubber (ACM Compounds) for Electric Transformer's Rubber Beads, Rubber Bars
| Hardness, Shore Durometers | 70±5 |
|
| Tensile Strength, MPa, Bigger Than | 12 |
|
| Maximum Tensile Elongation, %, Bigger Than | 200 |
|
| Compression Permanent Deformation | 125℃*24h, Air, %, Less Than | 35 |
| 125℃*168h, #25 Transformer Oil, %, Less Than | 45 |
|
| Tearing Strength, KN/m, Bigger Than | 20 |
|
| Anti #25 Transformer Oil, 125℃*24h | Volume Variation | -3%~+8% |
| Weight Variation | -5%~+10% |
|
| Hot Air Aging, 100℃*72h | Hardness Variation, Less Than | +10 |
| Tensile Strength Variation, %, Bigger Than | -20 |
|
| Breakage Elongation Variation, %, Bigger Than | -30 |
|
| Brittleness Temperature, ℃, Less Than | -35 |
|
| Compatibility with #25 Transformer Oil | Medium Consumption Rate Variation, %, Less Than | 1.0 |
| Surface Tension, Difference with Blank Test, MN/m | 0-2 |
|
| Acidity, mgKOH/g, Less Than | 0.3 |
|
| Ozone Aging Resistance, 50pphm, 40℃*72h, Static Stretch Tensile 15% | Non Cracks |
|